| Phenolic Epoxy résin spésifikasi Téknis | Métode bungkusan | Aplikasi | |||||||||||||
| Modél | Warna | Wangun | Kandungan Padet (%) | EEW (g/eq) | Titik Lelembutan (℃) | Kromatisitas (G/H) | Viskositas (mPa·s) | Hydrolyzable Klorin (ppm) | Kandungan Bromin (%) | Kandungan Fosfor (%) | Sampel | ||||
| Résin Époksi Phenolik | BNE Bisphenol A fénol formaldehida | EMTE200 | Teu warnaan ka Konéng Lampu | Padet | - | 200-220 | 62-68 | G＜2 | - | ≤200 | - |  | Kantong kertas sareng liner PE jero: 25 kg / kantong. | Laminasi clad tambaga éléktronik, laminates éléktronik, elém tahan panas, bahan komposit, palapis tahan suhu luhur, rékayasa sipil sareng tinta éléktronik, jsb. | |
| EMTE200H | 190-220 | 65-75 | G≤3 | - | ≤200 | - | |||||||||
| EMTE 200A80 | Cairan | 80±1.0 | 190-220 | - | G≤2 | 1100-180 | ≤200 |  | Drum beusi: 220kg/drum | ||||||
| PNE fénol novolac résin époksi | EMTE625 | Teu warnaan ka Konéng Lampu | Cairan | - | 164-177 | - | G≤1 | 9000-13000 | ≤300 | - | Drum beusi: 220kg/drum | Laminasi clad tambaga éléktronik, laminates éléktronik, elém tahan panas, bahan komposit, palapis tahan suhu luhur, rékayasa sipil sareng tinta éléktronik, jsb. | |||
| EMTE636 | 170-173 | 28-30 | G≤0.8 | - | ≤200 |  | |||||||||
| EMTE636L | 169-173 | 23-27 | G≤1 | ≤300 | - | ||||||||||
| EMTE637 | 170-174 | 31-36 | G≤0.8 | ≤250 | - | ||||||||||
| EMTE 638A80 | 170-180 | 80±1 | G≤0.8 | 100-280 | ≤200 | - | |||||||||
| EMTE638 | 171-175 | 36-40 | G≤0.5（0.6） | 35-39 | 80-180 |  | |||||||||
| EMTE638S | 171-175 | 31-35 | G≤0.5 | - | ≤200 | - | |||||||||
| EMTE639 | 174-180 | 44-50 | G≤1 | ≤300 | - | ||||||||||
| CNE o-Kresol aldehida résin époksi | EMTE701 | Teu warnaan ka Konéng Lampu | Padet | 196-206 | 65-70 | G＜2 | <500 | - | Kantong kertas sareng liner PE jero: 25 kg / kantong. | Laminasi clad tambaga éléktronik, laminates éléktronik, elém tahan panas, bahan komposit, palapis tahan suhu luhur, rékayasa sipil sareng tinta éléktronik, jsb. | |||||
| EMTE702 | 197-207 | 70-76 | G＜2 | <500 | - | ||||||||||
| EMTE704 | 200-215 | 88-93 | G＜2 | <1000 | - | ||||||||||
| EMTE704M | 200-215 | 87±1 | G＜2 | 40-100 |  | ||||||||||
| EMTE704ML | 200-210 | 80-85 | G＜2 | <1000 | - | ||||||||||
| EMTE704L | 207-215 | 78-83 | G＜2 | <1000 | - | ||||||||||